SMT Solder Paste Manufacturers.
Focused on SMT soldering processes, a one-stop electronic soldering solutions provider.
Here you can find knowledge about Solder Bar 25kg, including but not limited to usage methods, installation techniques, troubleshooting and more. Focused on SMT soldering processes. If you can't find what you need, please contact us anytime.
Void-free nitrogen reflow combined with low-void solder paste can reduce the void ratio of BGA solder joints from 15% to below 3%. This combination has been stably running on Jia Jinyuan's production line for over 2 million units. The key is that nitrogen purity must be maintained above 99.995% with oxygen content below 50 ppm. Combined with the thixotropy optimization and activator gradient volatilization design of Jia Jinyuan LDS-702 low-void solder paste, voids are effectively suppressed in the early stage of reflow.
Published: 2025-05-26Solder sample testing should focus on four practical dimensions: printing accuracy, wetting and spreading capability, void rate control, and solder ball formation tendency. Through methods such as stencil aperture matching verification, post-reflow solder joint morphology observation, X-ray void area statistics, and solder ball counting under a microscope, the adaptation boundaries of Jia Jinyuan solder under different PCB pad designs and process windows can be quickly identified.
Published: 2025-05-15
In manual soldering, the selection of solder wire diameter directly affects drag soldering efficiency and solder joint formation quality. Thick solder wire is suitable for large-area pads and quick solder replenishment but is prone to causing bridging, while thin solder wire facilitates precise pin control but imposes higher requirements on operation rhythm. Actual production lines need to comprehensively weigh factors based on PCB pad size, component spacing, and operation takt time.
Published: 2025-05-11Pin dip soldering using tin bars for molten tin is an efficient process for high-volume component preprocessing. It achieves uniform tin plating on pin surfaces through constant-temperature bath control, pre-coating of flux, and vertical immersion, significantly improving subsequent SMT placement yield and reflow soldering wettability. Jiajinyuan tin bars exhibit stable fluidity and minimal dross in the 183°C–205°C range, meeting the continuous operation requirements of pre-wave soldering processes.
Published: 2025-04-20During the soldering rework of gold-plated boards, the gold layer is prone to oxidation by high temperatures or loss due to mechanical scraping, which leads to exposure of the nickel layer on the pad surface, poor wetting, and increased cold solder joints, directly affecting the long-term reliability of gold-plated board soldering. It is necessary to implement coordinated control from three aspects: soldering iron temperature, dwell time, and cleaning method.
Published: 2025-03-09Thick copper board welding must address three major challenges: large heat capacity, rapid heat dissipation, and difficult wetting caused by copper surface oxidation. During the SMT placement stage, the reflow peak temperature must be increased to 265℃±3℃ and the time above the liquidus line must be extended to over 90 seconds. For wave soldering, a combination of high-activity no-clean flux with a preheating temperature of 150℃, wave height of 10mm, and conveyor angle of 5° must be used. Otherwise, cold solder joints, excessive solder joint void rates, and pad peeling on thick copper PCBs are highly likely to occur.
Published: 2025-02-16Eutectic solder Sn63Pb37 solder wires and bars are the preferred material for reworking high-density devices such as BGA and QFN in the repair industry, thanks to their precise 183°C melting point, absence of pasty range, and excellent wettability. Jia Jinyuan's products of this model have demonstrated extremely low bridging rates and stable tensile strength values in actual production lines. With common diameter specifications ranging from 0.5mm to 1.2mm, they meet the dual requirements of manual soldering iron welding and hot air gun solder replenishment.
Published: 2025-02-02
The voids in solder joints formed by bar solder wave soldering are closely related to the material properties of the solder bar. Excessive impurity elements such as arsenic and antimony in high-purity lead-free solder bars will significantly aggravate void formation, while an imbalanced tin-copper alloy ratio or fluctuations in silver content directly affect the surface tension and wetting behavior in the molten state, thereby altering the gas escape paths inside the solder joint.
Published: 2025-01-19Medical electronic equipment has extremely stringent requirements for the purity, ionic residue and long-term reliability of solder materials. With its strictly controlled metal composition, low halogen content and batch stability, ISO solder materials have become the first choice for SMT production lines of implantable and monitoring devices. Jiajinyuan ISO solder materials have passed the biocompatibility pre-assessment of IEC 60601-1 Appendix A. In actual production lines, the ionic residue on the board surface after reflow is <0.85μg/cm2, and the copper mirror corrosion test shows no discoloration for over 72 hours.
Published: 2025-01-15
In 2024, solder paste suppliers accelerated intelligent R&D, promoted the deep integration of online inspection and process parameter optimization technologies, improved manufacturing efficiency and product quality, and injected new impetus into the electronics manufacturing industry.
Published: 2025-01-08Our technical team is always ready to provide professional solder material selection advice and SMT process solutions.